Application
Our Pani coatings are tailor-made for steel structures erecting at diverse harsh environments.
Our water-borne adhesives are with extremely low VOC emissions, odor-free, high-bonding strength and widely used in train transit and automotive interior decorations.
Bridges, tunnels, rail transportation, ships, nearshore port facilities, offshore wind farms, water conservancy projects, communication base stations, power grids, transmission towers, onshore steel structures, offshore drilling platforms, and other major equipment and infrastructure facilities.
(C4) Bridges
(C4) Oceanic Wind-mills for power generation
(C3) Sea Containers
(CX) Ocean-carriers
(C5) Oceanic Drilling Platforms
(C3) Highway Guard-rails
| Test Parameters |
C4
Standard & Limits
Polyaniline Complete Coating System (80+110+40μm) |
C5
Standard & Limits
Polyaniline Complete Coating System (80+160+80=320μm) |
CX
Standard & Limits
Polyaniline Complete Coating System (80+160+80=320μm) |
|---|---|---|---|
| Neutral Salt Spray (NSS) | 2000hr no blistering, no peeling, no rusting, no cracking |
3000hr no blistering, no peeling, no rusting, no cracking |
4000hr no blistering, no peeling, no rusting, no cracking |
| One-sided Creepage from Scribe | 0.5mm |
0.5mm |
0.5mm, long-term stable |
| UV B313 Aging | 3000hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 2 |
3000hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 2 |
4000hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 2 |
| Xenon-arc Aging | 3000hr ΔE≤2.2, retention ≥87% |
4000hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 2 |
5000hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 2 |
| Cross-cut Adhesion | Stable 0–1 Grade |
Stable Grade 0 |
Stable Grade 0, Compliant |
| Pull-off Adhesion | >15MPa |
>15MPa |
>15MPa |
| Water Immersion Resistance | 240hr no blistering, no peeling, no chalking, no cracking; color change grade 1, gloss loss grade 0 |
480hr no blistering, no peeling, no chalking, no cracking; color change grade 0, gloss loss grade 1 |
720hr no blistering, no peeling, no chalking, no cracking; color change grade 0, gloss loss grade 1 |
| Acid Immersion Resistance | 240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
| Alkali Immersion Resistance | 240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
240hr no blistering, no peeling, no rusting, no cracking; color change grade 0, gloss loss grade 0 |
| 180° Bend Test | Hairline cracks, no peeling |
Hairline cracks, no peeling |
3mm hairline cracks, no peeling |
| Impact Energy | ≥0.62J no chipping |
≥0.72J no chipping |
≥0.85J no chipping |